I-LQS01 i-Post Consumer Recycling Polyolefin Shrink Film
Intshayelelo yeMveliso
Ukwazisa inguqulelo yethu yamva nje kwizisombululo zokupakisha ezizinzileyo - ifilimu ye-pololefin shrink equlethe i-30% yemathiriyeli ehlaziyiweyo yabathengi. Le filimu ye-cutting-edge ye-shrink yenzelwe ukuhlangabezana nemfuno ekhulayo yezinto zokupakisha ezihambelana nokusingqongileyo ngaphandle kokubeka esichengeni umgangatho kunye nokusebenza.
1.Iifilimu zethu ze-polyolefin ezicuthayo zibonisa ukuzinikela kwethu kuzinzo lokusingqongileyo kunye neendlela ezinoxanduva lokuvelisa. Ngokusebenzisa i-30% yezinto ezisetyenzisiweyo ezisetyenzisiweyo, siyakwazi ukunciphisa impembelelo yokusingqongileyo yeemveliso zethu zokupakisha ngelixa sikhuthaza uqoqosho lwesetyhula.
2.Yintoni eyenza ifilimu yethu ye-polyolefin ishwabene ngokwahlukileyo kukukwazi kwayo ukuhambisa ukusebenza okuphezulu ngelixa ixhasa iinjongo zozinzo. Ifilimu iveliswa kusetyenziswa inkqubo efanayo yokuvelisa njengefilimu yethu ye-G10l, iqinisekisa umgangatho ongaguqukiyo kunye nokusebenza abathengi bethu baye baxhomekeke kuyo. Iimpawu ezintle zefilimu zefilimu, ukutywinwa kobushushu obugqwesileyo, ukunyuswa okuphezulu kunye nokuhambelana neentlobo ezahlukeneyo zoomatshini bokupakisha zibonelela ngokuthembeka kunye nokuguquguquka okufunekayo kwiinkqubo ezahlukeneyo zokupakisha.
3.Ukongeza kumsebenzi wayo oncomekayo, ifilimu yethu ye-polyolefin shrink ifumene isatifikethi se-GRS 4.0 ebalaseleyo, esibonisa ukuthotyelwa kwemigangatho yehlabathi yokurisayikilisha. Isiqinisekiso singqina umgangatho ophezulu wefilim womxholo ohlaziyiweyo kunye nokubambelela kwayo kwimigangatho engqongqo yokusingqongileyo kunye nentlalo kuyo yonke imveliso yayo.
4.Ngokukhetha iifilimu zethu ze-polyolefin shrink, amashishini angenza igalelo elibonakalayo ekuzinzeni ngaphandle kokuncama ukusebenza kunye nokubhenela kokupakishwa kwawo. Nokuba isetyenziselwa ukuthengisa iimveliso, ukupakishwa kokutya okanye usetyenziso lwamashishini, ifilimu ibonelela ngezisombululo zokupakisha ezizinzileyo ezihambelana nexabiso labathengi kunye namashishini abakhathalela indalo.
I-5.Siyaqonda ukubaluleka kokubonelela ngezisombululo zokupakisha ezingafezekisi kuphela iimfuno zeemarike zanamhlanje, kodwa zinegalelo kwikamva elizinzileyo. Ifilimu yethu ye-pololefin shrink iqulethe i-30% yesiqulatho esenziwe ngokutsha sabathengi kwaye sinebhongo ngokunikezela ngemveliso ebonisa ukuzinikela kwethu ekusunguleni izinto ezintsha, umgangatho kunye noxanduva lokusingqongileyo.
Sijoyine ekuthatheni indlela ezinzileyo yokupakisha ngefilimu eshwabeneyo yepolyolefin. Ngokubambisana, sinokuba nefuthe elihle kwindalo ngelixa sihambisa izisombululo zokupakisha ezihlangabezana nemigangatho ephezulu yokusebenza kunye nokuzinza.
Ukutyeba: 15 micron, 19 micron, 25 micron.
I-LQS01 I-POST CONSUMER RECYCATION POLYOLEFIN SHRINK FILM | |||||||||||
INTO YOVAVANYO | IYUNITHI | UVAVANYO lwe-ASTM | IINDLELA EZIQHELEKILEYO | ||||||||
INTSHAYELELO | |||||||||||
IPost Consumer Recycling | I-30% yePolyethylene yasemva komthengi esetyenzisiweyo kwakhona (RM0193) | ||||||||||
UKUTYA | 15um | 19um | 25um | ||||||||
I-TENSILE | |||||||||||
Amandla okuqina (MD) | N/mm² | D882 | 115 | 110 | 90 | ||||||
Amandla okuqina (TD) | 110 | 105 | 85 | ||||||||
Elongation(MD) | % | 105 | 110 | 105 | |||||||
Ubude (TD) | 100 | 105 | 95 | ||||||||
INYEMBEZI | |||||||||||
MD kwi-400gm | gf | D1922 | 10.5 | 13.5 | 16.5 | ||||||
TD kwi-400gm | 9.8 | 12.5 | 16.5 | ||||||||
AMANDLA otywiniweyo | |||||||||||
MD\Hot Wire Seal | N/mm | F88 | 0.85 | 0.95 | 1.15 | ||||||
TD\Hot Wire Seal | 1.05 | 1.15 | 1.25 | ||||||||
I-COF (ifilimu ifilimu) | - | ||||||||||
I-Static | D1894 | 0.20 | 0.18 | 0.22 | |||||||
Unamandla | 0.20 | 0.18 | 0.22 | ||||||||
I-OPTIS | |||||||||||
Inkungu | D1003 | 3.5 | 3.8 | 4.0 | |||||||
Ukucaca | D1746 | 93.0 | 92.0 | 91.0 | |||||||
Iglosi @ 45Deg | D2457 | 85.0 | 82.0 | 80.0 | |||||||
UMTHETHO | |||||||||||
Izinga loThutho lwe-Oxygen | cc/㎡/ngosuku | D3985 | 9200 | 8200 | 5600 | ||||||
Izinga loThutho loMphunga waManzi | gm/㎡/ngosuku | F1249 | 25.9 | 17.2 | 14.5 | ||||||
IPROPATI YOKUSHINGA | MD | TD | MD | TD | |||||||
Ukushwabana kwamahala | 100℃ | % | D2732 | 17 | 26 | 14 | 23 | ||||
110℃ | 32 | 44 | 29 | 42 | |||||||
120℃ | 54 | 59 | 53 | 60 | |||||||
130℃ | 68 | 69 | 68 | 69 | |||||||
MD | TD | MD | TD | ||||||||
Shrink Tension | 100℃ | Mpa | D2838 | 1.65 | 2.35 | 1.70 | 2.25 | ||||
110℃ | 2.55 | 3.20 | 2.65 | 3.45 | |||||||
120℃ | 2.70 | 3.45 | 2.95 | 3.65 | |||||||
130℃ | 2.45 | 3.10 | 2.75 | 3.20 |