Isu tinofara kuburitsa hunyanzvi hwedu hwazvino mukurongedza tekinoroji -LQG303general chinangwa shrink firimu. Iine advanced cross-linking tekinoroji, iyi inochinjika shrink firimu rakagadzirirwa kusangana neakasiyana ekurongedza anodikanwa emaindasitiri akasiyana. Kunyangwe iwe uri muchikamu chezvekudya, chinwiwa, chemishonga kana chevatengi,LQG303ndiyo mhinduro yakakwana kune ako ese ekurongedza zvinodiwa.
1.LQG303universal shrink firimu rakanyatsogadzirwa kuti rive rakanyanya-ushamwari, rine shrinkage yakanakisa uye kupisa-kuburikidza nekuramba. Izvi zvinoreva kuti iwe unogona kuwana chisimbiso chakasimba uye yakafara yekuisa chisimbiso tembiricha, kuve nechokwadi chekuti zvigadzirwa zvako zvakachengetedzwa zvakachengeteka uye zvakachengetedzwa panguva yekutumira uye kuchengetedza. Pamusoro pezvo, iyo firimu inopa yakanakisa puncture uye kubvarura kuramba, ichipa yakawedzera kusimba kune ako akaputirwa zvinhu.
2.Chimwe chezvakakosha zveLQG303firimu ndiyo inoshamisa shrinkage rate inosvika 80%. Uku kukwidziridzwa shrink kugona kunoita kuti zvigadzirwa zvako zvakanyatsorongedzerwa kune inyanzvi uye inotaridzika kutaridzika. Kunyangwe iwe uri kurongedza zvinhu zvega kana kubatanidza zvigadzirwa zvakawanda pamwechete,LQG303firimu rinopa kusakwana kwekurongedza kuita uye rinowedzera kuratidzwa kwese kwechigadzirwa chako.
3. LQG303universal shrink firimu rinoenderana neanenge ese ekurongedza masisitimu ari kushandiswa parizvino, zvichiita kuti ive yekuwedzera isina musono kune yako iripo yekurongedza maitiro. Kuchinjika kwayo uye nyore kushandisa kunoita kuti ive yakanaka kune mabhizinesi ari kutsvaga kugadzirisa mashandiro avo ekurongedza pasina kurongeka patsva kana kukwidziridzwa kwemidziyo.
4. LQG303general chinangwa shrink firimu ishanduko yemutambo munyika yekurongedza. Zvimiro zvayo zvepamusoro, zvinosanganisira shrinkage yakanakisa, kupisa-kuburikidza nekupikisa uye kuenderana nemhando dzakasiyana-siyana dzekurongedza, ita kuti ive sarudzo yekutanga kune mabhizinesi anotsvaga akavimbika, anobudirira ekurongedza mhinduro.LQG303general shrink firimu uye uvandudze kunaka kwekurongedza kwezvigadzirwa zvako.
Ukobvu: 12 micron, 15 micron, 19 micron, 25 micron, 30 micron, 38 micron, 52 micron.
LQG303 CROSS-LINKED POLYOLEFIN SHRINK FILM | ||||||||||||||||||||||
TEST ITEM | UNIT | ASTM TEST | ZVINOKOSHA ZVAKAWANDA | |||||||||||||||||||
KUKORA | 12um | 15um | 19um | 25um | 30um | 38um | 52um | |||||||||||||||
TENSILE | ||||||||||||||||||||||
Tensile Simba (MD) | N/mm² | D882 | 130 | 135 | 135 | 125 | 120 | 115 | 110 | |||||||||||||
Tensile Simba (TD) | 125 | 125 | 125 | 120 | 115 | 110 | 105 | |||||||||||||||
Elongation(MD) | % | 115 | 120 | 120 | 120 | 125 | 130 | 140 | ||||||||||||||
Elongation (TD) | 105 | 110 | 110 | 115 | 115 | 120 | 125 | |||||||||||||||
MISODZI | ||||||||||||||||||||||
MD pa400gm | gf | D1922 | 11.5 | 14.5 | 18.5 | 27.0 | 32.0 | 38.5 | 41.5 | |||||||||||||
TD pa400gm | 12.5 | 17.0 | 22.5 | 30.0 | 35.0 | 42.5 | 47.5 | |||||||||||||||
SIMBA SIMBA | ||||||||||||||||||||||
MD\Hot Wire Seal | N/mm | F88 | 1.13 | 1.29 | 1.45 | 1.75 | 2.15 | 2.10 | 32 | |||||||||||||
TD\Hot Wire Seal | 1.18 | 1.43 | 1.65 | 1.75 | 2.10 | 2.10 | 33 | |||||||||||||||
COF (Firimu Kune Firimu) | - | |||||||||||||||||||||
Static | D1894 | 0.23 | 0.19 | 0.18 | 0.22 | 0.23 | 0.25 | 0.21 | ||||||||||||||
Dynamic | 0.23 | 0.19 | 0.18 | 0.22 | 0.23 | 0.25 | 0.2 | |||||||||||||||
OPTICS | ||||||||||||||||||||||
Haze | D1003 | 2.3 | 2.6 | 3.5 | 3.8 | 4.2 | 4.8 | 4.2 | ||||||||||||||
Kujeka | D1746 | 98.5 | 98.8 | 98.0 | 97.5 | 94.0 | 92.0 | 97.5 | ||||||||||||||
Kubwinya @ 45Deg | D2457 | 88.5 | 88.0 | 87.5 | 86.0 | 86.0 | 85.0 | 84.5 | ||||||||||||||
CHIDZINGIKO | ||||||||||||||||||||||
Oxygen Transmission Rate | cc/㎡/zuva | D3985 | 10300 | 9500 | 6200 | 5400 | 4200 | 3700 | 2900 | |||||||||||||
Mvura Vapor Transmission Rate | gm/㎡/zuva | F1249 | 32.5 | 27.5 | 20.5 | 14.5 | 11 | 9.5 | 8.5 | |||||||||||||
SHRINKAGE PROPERTIES | MD | TD | MD | TD | MD | TD | ||||||||||||||||
Free Shrinkage | 100 ℃ | % | D2732 | 17.5 | 27.5 | 16.0 | 26.0 | 15.0 | 24.5 | |||||||||||||
110 ℃ | 36.5 | 44.5 | 34.0 | 43.0 | 31.5 | 40.5 | ||||||||||||||||
120 ℃ | 70.5 | 72.0 | 68.5 | 67.0 | 65.5 | 64.5 | ||||||||||||||||
130 ℃ | 81.0 | 79.5 | 80.0 | 79.0 | 80.5 | 80.0 | ||||||||||||||||
MD | TD | MD | TD | MD | TD | |||||||||||||||||
Shrink Tension | 100 ℃ | Mpa | D2838 | 2.30 | 2.55 | 2.70 | 2.85 | 2.65 | 2.85 | |||||||||||||
110 ℃ | 2.90 | 3.85 | 3.40 | 4.10 | 3.35 | 4.05 | ||||||||||||||||
120 ℃ | 3.45 | 4.25 | 3.85 | 4.65 | 3.75 | 4.55 | ||||||||||||||||
130 ℃ | 3.20 | 3.90 | 3.30 | 4.00 | 3.55 | 4.15 |