LQS01 Post Consumer Recycling Polyolefin Shrink Film
Okwu Mmalite ngwaahịa
Na-ewebata ihe ọhụrụ ọhụrụ anyị na ngwọta nkwakọ ngwaahịa na-adigide - ihe nkiri polyolefin shrink nwere 30% ihe eji emegharị ihe. Emebere ihe nkiri a na-egbu egbu nke ukwuu iji gboo mkpa na-eto eto maka ihe nkwakọ ngwaahịa enyi na gburugburu ebe obibi na-emebighị mma na arụmọrụ.
1.Our polyolefin shrink film na-egosi nkwa anyị maka nkwado gburugburu ebe obibi na ọrụ mmepụta ihe. Site n'iji 30% emegharịrị ihe eji emegharị ihe, anyị na-enwe ike ibelata mmetụta gburugburu ebe obibi nke ngwaahịa nkwakọ ngwaahịa anyị ka anyị na-akwalite akụ na ụba okirikiri.
2.What esetịpụ anyị polyolefin shrink film iche bụ ike ya napụta elu arụmọrụ mgbe na-akwado nkwado ihe mgbaru ọsọ. A na-emepụta ihe nkiri ahụ site na iji otu usoro mmepụta ihe dị ka ihe nkiri G10l anyị, na-eme ka ịdị mma na arụmọrụ ndị ahịa anyị na-adabere na ya. Ihe eji arụ ọrụ nke ọma nke ihe nkiri ahụ, ihe mkpuchi ọkụ dị mma, nkwụsịtụ dị elu na ndakọrịta na igwe nkwakọ ngwaahịa dị iche iche na-enye ntụkwasị obi na ntụgharị dị mkpa maka ngwa ngwa ngwa ngwa.
3.Na mgbakwunye na arụmọrụ ya dị egwu, ihe nkiri polyolefin shrink anyị enwetala asambodo GRS 4.0 a ma ama, na-egosipụta nrube isi na ụkpụrụ nrụpụta ụwa. Asambodo a na-egosi na ihe nkiri a nwere ọkwa dị elu nke ihe ejigharịgharị ya na nrube isi na ụkpụrụ gburugburu ebe obibi na mmekọrịta ọha na eze n'oge mmepụta ya.
4.By ị na-ahọrọ polyolefin shrink films, ulo oru nwere ike ime ka a tangible onyinye na nkwado na-enweghị ịchụ àjà ọrụ na mkpesa nke ha nkwakọ. Ma ejiri ya maka ngwaahịa ndị na-ere ahịa, nkwakọ nri ma ọ bụ ngwa ụlọ ọrụ mmepụta ihe, ihe nkiri ahụ na-enye ngwọta nkwakọ ngwaahịa na-adịgide adịgide nke kwekọrọ na ụkpụrụ nke ndị na-azụ ahịa na azụmahịa na gburugburu ebe obibi.
5.We ghọtara mkpa ọ dị ịnye ngwọta nkwakọ ngwaahịa na-abụghị nanị na-egbo mkpa nke ahịa taa, ma na-enye aka n'ọdịnihu na-adigide. Ihe nkiri polyolefin shrink anyị nwere 30% ọdịnaya emegharịrị ndị na-azụ ahịa ma anyị ji mpako na-enye ngwaahịa na-egosipụta nrara anyị raara onwe anyị nye ihe ọhụrụ, ịdịmma na ọrụ gburugburu ebe obibi.
Soro anyị na-eme usoro na-adigide maka nkwakọ ngwaahịa na fim shrink polyolefin. Ọnụ, anyị nwere ike inwe mmetụta dị mma na gburugburu ebe obibi mgbe anyị na-ebuga ngwọta nkwakọ ngwaahịa na-ezute ụkpụrụ kachasị elu nke arụmọrụ na nkwado.
Ọkpụrụkpụ: 15 micron, 19 micron, 25 micron.
LQS01 ndị ahịa biputere ihe nkiri POLYOLEFIN SHRINK | |||||||||||
Nnwale ihe | UNIT | Nnwale ASTM | URU NDỊ MMADỤ | ||||||||
Okwu mmalite | |||||||||||
Mgbagharị ndị ahịa biputere | 30% polyethylene megharịrị ndị ahịa mgbe emegharịrị (RM0193) | ||||||||||
Okpokoro | 15um | 19um | 25um | ||||||||
TENSILE | |||||||||||
Ike tensile (MD) | N/mm² | D882 | 115 | 110 | 90 | ||||||
Ike tensile (TD) | 110 | 105 | 85 | ||||||||
elongation(MD) | % | 105 | 110 | 105 | |||||||
Ogologo oge (TD) | 100 | 105 | 95 | ||||||||
AKWỤKWỌ | |||||||||||
MD na 400 g | gf | D1922 | 10.5 | 13.5 | 16.5 | ||||||
TD na 400 g | 9.8 | 12.5 | 16.5 | ||||||||
Ike akara | |||||||||||
MD \ Hot Waya Akara | N/mm | F88 | 0.85 | 0.95 | 1.15 | ||||||
TD\ Hot Waya akara | 1.05 | 1.15 | 1.25 | ||||||||
COF (ihe nkiri gaa na ihe nkiri) | - | ||||||||||
Static | D1894 | 0.20 | 0.18 | 0.22 | |||||||
Dị ike | 0.20 | 0.18 | 0.22 | ||||||||
OPTIC | |||||||||||
Ofufe | D1003 | 3.5 | 3.8 | 4.0 | |||||||
Ido anya | D1746 | 93.0 | 92.0 | 91.0 | |||||||
Gloss @ 45Deg | D2457 | 85.0 | 82.0 | 80.0 | |||||||
Mgbochi | |||||||||||
Ọnụego nnyefe oxygen | cc/㎡/ụbọchị | D3985 | 9200 | 8200 | 5600 | ||||||
Ọnụego mbufe uzuoku mmiri | gm/㎡/ụbọchị | F1249 | 25.9 | 17.2 | 14.5 | ||||||
AKWỤKWỌ MMADỤ | MD | TD | MD | TD | |||||||
Mbelata efu | 100 ℃ | % | D2732 | 17 | 26 | 14 | 23 | ||||
110 ℃ | 32 | 44 | 29 | 42 | |||||||
120 ℃ | 54 | 59 | 53 | 60 | |||||||
130 ℃ | 68 | 69 | 68 | 69 | |||||||
MD | TD | MD | TD | ||||||||
Mbelata Esemokwu | 100 ℃ | Mpa | D2838 | 1.65 | 2.35 | 1.70 | 2.25 | ||||
110 ℃ | 2.55 | 3.20 | 2.65 | 3.45 | |||||||
120 ℃ | 2.70 | 3.45 | 2.95 | 3.65 | |||||||
130 ℃ | 2.45 | 3.10 | 2.75 | 3.20 |